نانوتکنولوژی - n Situ Study of Phase Transformations during Non-Isothermal Tempering of Bainitic and Martensitic Microstructures
یکشنبه 26 شهریور 1396  08:53 ب.ظ    ویرایش: یکشنبه 26 شهریور 1396 08:54 ب.ظ

Phase transformations during non-isothermal tempering of bainitic or martensitic microstructures obtained after quenching of a medium-carbon low-alloy steel was studied. The microstructures correspond to different locations of an as-quenched large-sized forged ingot used as a die material in the automotive industry. High-resolution dilatometry experiments were conducted to simulate the heat treatment process, as well as to investigate different phenomena occurring during non-isothermal tempering. The microstructures were characterized using optical and scanning electron microscopy. Dilatometry analyses demonstrated that tempering behavior varied significantly from bainitic to martensitic microstructures. Retained austenite, which exists between bainitic ferrite sheaves, decomposes to lower bainite causing a remarkable volume increase. It was found that this decomposition finishes below 386 °C. By contrast, martensite tempering was accompanied with a volume decrease due to the decomposition of medium-carbon martensite to low carbon
martensite and carbides.
http://www.mdpi.com/2075-4701/7/9/346

   


نظرات()   

نانوتکنولوژی